304L Stainless Steel Bar

Phone : +0086 17695537635

Whatsapp : +86 17695537635

Email : pery@tjlinggang.com

Product Description

Product Display

Spot Warehouse

Packaging and Transportation

304L Stainless Steel Bar Description

304L stainless steel bar is used where welding is involved, as a variant of 304 stainless steel bar. The lower carbon content greatly lowers the precipitation of carbides in the heat-affected zone close to the weld, and such precipitation is likely to lead to intergranular corrosion of stainless steel in certain settings. Basically, their is no need to anneal weld joints prior to using the completed metal form using 304L, saving time and effort. As a matter of fact, both 304 and 304L stainless steel bars can be used for many of the same applications. The differences are often minor enough that one isn’t considered massively more useful over the other. 304L stainless steel bars are commonly used as manufacturing parts in fields such as food processing equipment, building materials, automobile parts.

Product Parameters

Product Name		304L Stainless Steel Bar
Type		Steel Bar
Outer Diameter	Round Bar	4mm-500mm
	Hexagon Bar	18mm-57mm (11/16″ to 2-3/4″)
	Square Bar	18mm-47mm (11/16″ to 1-3/4″)
	Flat Steel	1/2 "to 10", Thickness: 2mm-150mm, Can provide customized
Length		1-6 meters, Length can be customized
Standard		ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface		Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc.
Scope of Application		Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc.

Chemical Composition

C	Si	Mn	Cr	Ni	S	P
≤ 0.03	≤1.0	≤ 2.0	18.0～20.0	8.0～12.0	≤ 0.03	≤ 0.035

Mechanical Properties

Tensile Strength Kb (MPa)	Yield Strength σ0.2 (MPa)	Elongation D5 (%)	Hardness
≥ 520	≥ 205	≥ 40	≤ 187HB ;≤ 90HRB;≤ 200HV

Physical Performance

Density(g/cm³)	Modulus of Elasticity(Gpa)	Coefficient of Thermal Expansion(10-6/°C)	Coefficient of Thermal Conductivity(W/m*K)	Resistivity(ΜΩ. cm)
8.03	193	16.9	16.2	72