Product Description

Product Display

Spot Warehouse

Packaging and Transportation

The chemical composition of A36 steel plate is mainly composed of iron, carbon, silicon, manganese, phosphorus, sulfur and other elements. Among them, iron is the most important component, accounting for more than 99% of the entire chemical composition. The carbon content is relatively high, generally around 0.2%, ensuring that the steel has a certain hardness and toughness. The addition of silicon, manganese and other elements enhances the strength and toughness of steel. The content of elements such as phosphorus and sulfur is low to ensure that the steel plate has good welding performance and corrosion resistance. A36 steel plate has excellent mechanical properties, and its tensile strength, yield strength, elongation and impact toughness are all higher than ordinary steel.

Product Parameters

Product Name	A36/Q235/S235JR Carbon Steel Plate
Production Process	Hot Rolling, Cold Rolling
Material Standards	AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc.
Width	100mm-3000mm
Length	1m-12m, or Customized Size
Thickness	0.1mm-400mm
Delivery Conditions	Rolling, Annealing, Quenching, Tempered or Standard
Surface Process	Ordinary, Wire Drawing, Laminated Film

Chemical Composition

C	Cu	Fe	Mn	P	Si	S
0.25~0.290	0.20	98.0	1.03	0.040	0.280	0.050

Mechanical Properties

A36

Limit Tensile Strength

Tensile Strength,

Yield Strength

Elongation at Break

(Unit: 200mm)

Elongation at Break

(Unit: 50mm)

Modulus of Elasticity

Bulk Modulus

(Typical for Steel)

Poisson's Ratio

Shear Modulus

Metric

400~550 MPa

250 MPa

20.0%

23.0 %

200 GPa

140 GPa

0.260

79.3 GPa

Imperial

58000~79800 psi

36300 psi

20.0%

23.0 %

29000 ksi

20300 ksi

0.260

11500 ksi

Physical Performance

Physical Performance	Metric	Imperial
Density	7.85 g/cm3	0.284 lb/in3

Scope of Application

Bolted, riveted or welded structures for bridges, buildings and oil drilling rigs.
Used for forming storage tanks, silos, bearing plates, fixtures, rings, templates, fixtures, sprockets, cams, gears, bottom plates, forgings, decoration engineering, piles, brackets, automobiles and agricultural equipment, frames, mechanical parts, etc.

Equivalent Material

National Standard GB	European Standard EN	American Standard ASTM	German Standard DIN, WNr	Japanese Standard JIS	French Standard AFNOR	British Standard BS	Canada HG
Q235B	S235JR	A283C	St37-2	SM400A	E24-2	40A/40B	230G
Italy UNI	India IS	Switzerland SS	Australia ONORM	Norway NS	Spain UNE	International Standards ISO	Portugal NP
Fe360B	IS2062	1311/1312	RSt360B	NS12123	AE235B-FN	E235B / Fe360B	FE360-B